Property | Unit | Test Method | Test Condition | Value |
Melt flow rate | ISO1133 | 190ºC/2.16Kg | g/10min | 2 |
The density of | ISO1183 | Kg/m³ | 0.921 | |
The melting temperature | GB/T19466.3 | ºC | 121 | |
Tensile yield strength | GB/T 1040.3 | MD | MPa | 10 |
GB/T 1040.3 | TD | MPa | 11 | |
Tensile breaking strength | GB/T 1040.3 | MD | MPa | 40 |
GB/T 1040.3 | TD | MPa | 33 | |
Tensile fracture nominal strain | GB/T 1040.3 | MD | % | 1200 |
GB/T 1040.3 | TD | % | 1400 | |
Tear strength | GB/T 16578.2 | MD | g | 220 |
GB/T 16578.2 | TD | g | 430 | |
Impact strength of falling dart | GB/T 9639.1 | g | 125 | |
Light transmittance | GB/T 2410 | % | 92 | |
The fog degree | GB/T 2410 | % | 14 | |
gloss | GB/T 8807 | % | 49 | |
Vica softening point | GB/T 1633 | ºC | 96 |