1. Product Description Modified PA6 is a high quality thermoplastic engineering plastic in the form of granulate for injection moulding and extrusion made by virgin PA6 materials.
Key feature:
30%GF High mechanical strength; Heat stabilized
Application:
Engine parts like intake manifold etc.
Data sheet is as below:
Property
Unit
Test standard
Test condition
GF reinforced PA6
BG6TBK-S02
Physical property
Density
g/cm3
ISO1183
1.36
Filler content
%
ISO 1172
GF30
Mold shrinkage
%
ISO 294
Parallel
0.2
Vertical
0.6
Mechanical property
Tensile strength
MPa
ISO 527
I type sample 50mm/min
180
Elongation at break
%
ISO 527
I type sample 50mm/min gauge length 50mm
3
Flexural strength
MPa
ISO 178
23ºC10mm/min
240
Flexural modulus
MPa
ISO 178
23ºC10mm/min
8500
Izod impact strength (notched)
KJ/m2
ISO 180
23ºC
16
Charpy impact strength (unnotched)
KJ/m2
ISO179
23ºC
95
Thermal property
Melting point
ºC
ISO11357-1
220
HDT
ºC
ISO 75
0.45Mpa
219
ISO 75
1.8Mpa
205
Flammability
Flammability
Class
UL-94
HB
GWIT
IEC 60695-2-13
-
Electrical property
Surface resistivity
Ω
IEC60093
1.00E+14
Volume resistivity
Ω·cm
IEC60093
1.00E+15
2. Applications Civilian and industrial high-spinning, conventional spinning, food-grade and medical-grade packing film, carpet yarn, fishing nets, ribbon, trimmer line, direct injection molding of engineering plastics, mechanical parts, high-loaded mechanical components, electric switchplugins, equipment, modification of composite materials, etc.